请教高手这几种异质结结构合理吗？ 结构优化是不是难以收敛？

wmg166

请教高手，这几种异质结结构合理吗？  哪种稳定些？ 哪种不稳定？    用vasp进行结构优化，先提示：VERY BAD NEWS! internal error in subroutine IBZKPT: Reciprocal lattice and k-lattice belong to different class of lattices. Often results are still useful...      48

后来正常计算：  计算100多步，没有收敛，进行续算了40步，出现这样的提示，是不是很难收敛？？？？
DAV:   4    -0.677931417870E+03    0.23458E-01   -0.38717E-01 32448   0.813E-01    0.560E-01
DAV:   5    -0.677934532166E+03   -0.31143E-02   -0.44420E-01 36224   0.117E+00    0.455E-01
DAV:   6    -0.677916415758E+03    0.18116E-01   -0.60129E-02 30464   0.619E-01    0.148E-01
DAV:   7    -0.677916216733E+03    0.19903E-03   -0.63223E-03 31104   0.155E-01    0.774E-02
DAV:   8    -0.677916127850E+03    0.88883E-04   -0.14543E-03 29440   0.771E-02    0.397E-02
DAV:   9    -0.677916131599E+03   -0.37491E-05   -0.37411E-04 30784   0.397E-02    0.205E-02
DAV:  10    -0.677916128392E+03    0.32067E-05   -0.72965E-05 30016   0.174E-02    0.814E-03
DAV:  11    -0.677916128778E+03   -0.38594E-06   -0.15902E-05 34496   0.881E-03    0.428E-03
DAV:  12    -0.677916128905E+03   -0.12631E-06   -0.42507E-06 29376   0.433E-03
  44 F= -.67791613E+03 E0= -.67790809E+03  d E =-.130047E+00
trial-energy change:   -0.130047  1 .order   -0.130681   -0.247990   -0.013371
step:   0.3105(harm=  0.3102)  dis= 0.03643  next Energy=  -677.916516 (dE=-0.130E+00)
bond charge predicted
       N       E                     dE             d eps       ncg     rms          rms(c)
DAV:   1    -0.677916498231E+03   -0.36945E-03   -0.10149E-01 23808   0.664E-01    0.622E-02